Here we are tearing up some fresh chassis yank flown in especially for the Lab via Raphael from Brazil, where the girls wear dental floss. :grin:
"But didn't you already destroy a couple of AM 16's?"
Yes. But this is entirely different.
These are out of (Raf, what are these out of again? )
Anyway, thay are full of the stickiest goop I have ever encountered. But that don't stop the show folks!
No way.
Can you spell Banded C Core?
Good.
Do C Cores usually come in high Ni?
Good. It is grain oriented.
Output cores carry a lot of flux. Which kind of steel handles more flux?
Good. You learned from all that destroyed iron.
Doc Hoyer even made some killer Peerless S-217-D outputs from a custom C Core that probably sounds better than the original.
No nickel to distort funny. Killer bass.
C cores are a superior design compared to most any lam. Especially when they are 4 mil. And they hold a gap quite nicely.
http://vacuumbrain.com/The_Lab/TA/Langevin/Raf/langevin_raf_3.jpg
"But didn't you already destroy a couple of AM 16's?"
Yes. But this is entirely different.
These are out of (Raf, what are these out of again? )
Anyway, thay are full of the stickiest goop I have ever encountered. But that don't stop the show folks!
No way.
Can you spell Banded C Core?
Good.
Do C Cores usually come in high Ni?
Good. It is grain oriented.
Output cores carry a lot of flux. Which kind of steel handles more flux?
Good. You learned from all that destroyed iron.
Doc Hoyer even made some killer Peerless S-217-D outputs from a custom C Core that probably sounds better than the original.
No nickel to distort funny. Killer bass.
C cores are a superior design compared to most any lam. Especially when they are 4 mil. And they hold a gap quite nicely.
http://vacuumbrain.com/The_Lab/TA/Langevin/Raf/langevin_raf_3.jpg